PrimaCreator Value Flex UV Resin - 500 ml - Black

https://www.fission3d.com/web/image/product.template/827/image_1920?unique=cb6faeb

50.00 € 50.0 EUR 50.00 €

50.00 €

Not Available For Sale

  • Brand
  • Color
  • Weight
  • Material

This combination does not exist.

Brand: Prima Creator
Color: Black
Weight: 500ml
Material: Flexible

Buy PrimaCreator Value Flex 3D printer Resin and get a good-value resin made from the best raw materials

PrimaCreator Value Flex Resin is a good-value resin made from the best raw materials. Realize good quality resin 3D prints at low costs. Flexible resin is the perfect resin when you are looking for high detail results that needs to have a very high impact strength. The shore hardness of 65-75 D together with an incredible elongation at break of 130% makes it a resin that can use in many applications and areas.

Main advantages of PrimaCreator Value Flex Resin:

  • Shore hardness of 65-75 D & elongation at break of 130%
  • 3D print high detail results that needs to have a very high impact strength
  • 3D print flexible objects with very small shrinkage
  • Optimized for UV Lightsource 395 – 405 nm.
  • Performs well on low powered DLP 3D printers
  • Fast curing time, 4 - 12 (depending on color) seconds per layer – for quicker prints

Cleaning of PrimaValue Flex 3D prints

After printing, clean your 3D print in IPA (Isopropyl Alcohol) to rinse off resin left on the model.

Curing the finished & washed 3D prints

When it´s time for curing you can use sunlight or a uv curing chamber.Depending on print the curing times can vary: In a UV light curing chamber, it will take about 2-5 minutes. In sunlight, 10-20 minutes. In daylight on a cloudy day, it can take up to 60 minutes.

Buy PrimaValue Flex Resin

When you want astonishing results for less cost than many other brands - PrimaCreator VALUE resin should be your first choice. Buy it now!


Flexural modulus 1.882 - 2.385 MPa 
Flexural strength  40-70 MPa
Hot deformation temp. 80 ℃
Thermal expansion 95*E-6
Volume shrinkage 3.72 - 4.24%
Linear shrinkage 1.05 - 1.35%
Tensile strength 30 - 52 MPa
Tensile modulus 1.779 - 2.385 MPa
Elongation at break 130%
Hardness (Shore D) 65 - 75D
Glass transition temp. 100 ℃
Density 1.05-1.25g/cm3
Notched impact strength 41-48 j/m
Viscosity 150-300 MPa·s   
Curing time 4 - 12s for layer thickness 0.05 mm
Bottom layer 40 - 60 s